GB/T 9756-2018: Synthetic resin emulsion coatings for interior wall
GB/T 9756-2018
GB
NATIONAL STANDARD OF THE
PEOPLE’S REPUBLIC OF CHINA
ICS 87.040
G 51
Replacing GB/T 9756-2009
Synthetic resin emulsion coatings for interior wall
合成树脂乳液内墙涂料
ISSUED ON. JUNE 7, 2018
IMPLEMENTED ON. JANUARY 1, 2019
Issued by. State Administration for Market Regulation;
Standardization Administration of the People's Republic of
China.
Table of Contents
Foreword ... 3
1 Scope ... 5
2 Normative references ... 5
3 Classification and grading ... 6
4 Requirements... 6
5 General requirements ... 7
6 Inspection rules ... 12
7 Marking, packaging and storage ... 13
Annex A (Normative) Method for testing anti-efflorescence ... 14
Foreword
This Standard was drafted in accordance with the rules given in GB/T 1.1-2009.
This Standard replaces GB/T 9756-2009, Synthetic resin emulsion coatings for
interior wall. Compared with GB/T 9756-2009, the major technical changes, in addition
to editorial changes, are as follows.
-- Change the scope of the standard (see Clause 1; Clause 1 of 2009 edition);
-- Delete the normative references including “GB/T 1250 and JC/T 412.1-2006” (see
Clause 2 of 2009 edition);
-- Add the normative references including “GB/T 6682-2008, GB/T 8170-2008 and
GB/T 23981-2009” (see Clause 2);
-- Add the items, indexes and test methods of low-temperature film-forming
properties of primers and finishes (see 4.1, 4.2 and 5.5.5);
-- Change the technical indexes of scrub resistance of film of finishes. the qualified
product’s acceptance index of scrub resistance of film of finishes is changed from
“≥ 300 times” into “≥ 350 times”, the first-class product’s index is changed from “≥
1000 times” into “1,500 times” and superior product’s index is changed from “≥
5,000” into “≥ 6,000” (see 4.2; 4.2 of 2009 edition);
-- Add the specifications of waterproof abrasive paper used for substrate polishing
and the inspection method for substrate flatness for the item of scrub resistance
of film (see 5.3);
-- Change the contents including wet-film thickness, sample density and unit of test
panel area in the calculation equation of primer brushing amount (see 5.4.2.1;
5.2.2.4 of 2009 edition);
-- Add the panel making requirements for the arbitration test for the items of contrast
ratio and scrub resistance of film (see 5.4.3.2);
-- Change the test panel thickness for the item of scrub resistance of film, from “430
mm × 150 mm × (4 ~ 6) mm” into “430 mm × 150 mm × 6 mm” (see Table 5; Table
5 of 2009 edition);
-- Add the requirements for brushes during the arbitration test for the item of scrub
resistance of film (see 5.5.11);
-- Add the processing requirements, when the PVA water solution for the item anti-
efflorescence has aggregation, precipitation, etc. during storage (see A.1.1.1;
A.1.1.1 of 2009 edition);
Synthetic resin emulsion coatings for interior wall
1 Scope
This Standard specifies the classification and grading, requirements, test methods,
inspection rules and marking, packaging and storage, etc. for synthetic resin emulsion
coatings for interior wall.
This Standard applies to coatings for interior wall, including primers and finishes, which
is based on synthetic resin emulsion, prepared with pigments, body pigments and all
kinds of auxiliaries and forms a thin coating layer with a smooth surface after
application.
2 Normative references
The following referenced documents are indispensable for the application of this
document. For dated references, only the edition dated applies to this document. For
undated references, the latest edition of the referenced documents (including all
amendments) applies to this document.
GB/T 1728-1979, Methods of test for drying time of coatings of paints and putties
GB/T 1766-2008, Paints and varnishes – Rating schemes of degradation of coats
GB/T 1910, Newsprint
GB/T 3186, Paints, varnishes and raw materials for paints and varnishes –
Sampling
GB/T 6682-2008, Water for analytical laboratory use – Specification and test
methods
GB/T 6750-2007, Paints and varnishes – Determination of density – Pycnometer
method
GB/T 8170-2008, Rules of rounding off for numerical values and expression and
judgement of limiting values
GB/T 9265-2009, Determination for alkali resistance of film of architectural paints
and coatings
method. place the long side of a straight ruler greater than 430 mm closely on the
surface of cement panels containing no asbestos fibre; then move along the long and
short sides, parallel to cement panels containing no asbestos fibre; observe the gap
between straight ruler and cement panels containing no asbestos fibre. If there is no
visible gap, then it meet the requirements for flatness.
5.4 Preparation of test sample panels
5.4.1 Sample preparation
When the dilution ratio is not indicated for products to tested, make panels after stirring
uniformly. When the dilution ratio is indicated for products to be tested, except for the
item of contrast ratio, panels needs to be made for the others to carry out the items of
inspection; panels shall be made after mixing uniformly in accordance with the dilution
ratio specified; if the proportion is within a range, an intermediate value shall be taken.
5.4.2 Preparation of primer test sample panels
5.4.2.1 Use the brush coating method for primers to make panels. First determine
density D of each sample as specified in GB/T 6750-2007; the brush coating-mass m
is calculated in accordance with equation (1).
where.
m – the value of one pass of brushing coating-mass of wet-film thickness 80 μm, in g;
D – the value of sample density after dilution in accordance with the dilution ratio
specified, in g/mL;
S – the value of sample panel area, in cm2;
k – 80 × 10-4, in cm.
Each pass of brushing coating-mass. the calculated brush coating-mass ± 0.1 g.
When, for some primers of low viscosity, it is impossible to make panels in accordance
with the calculated brush coating-mass, the brush coating-mass can be reduced as
appropriate, and the actual brush coating-mass shall be indicated in report; when, for
some primers, it is impossible to make panels in accordance with the calculated brush
coating-mass, then water shall be added to dilute, and the dilution ratio and actual
brush coating-mass shall be indicated in report.
5.4.2.2 Unless agreed otherwise, the type of base material, dimensions of test panel,
number of test panel, coating amount and curing periods of inspection items of primer
making-panels shall be as specified in Table 3.
5.5.3.1 Application property of primers
Use a brush to brush sample on the smooth surface of test panels; if there is no
difficulty in the movement of the brush, then it is assessed as “Without obstacle in
brush coating”.
5.5.3.2 Application property of finishes
Use a brush to brush sample on the smooth surface of test panels; control the coating
amount to the wet-film thickness about 100 μm. Make the long sides of test panel in
the horizontal direction; place the short sides vertically to form an angle of 85° to the
horizontal plane. After 6 h, use the same method to brush the second pass of sample;
if, during the second pass of brush coating, there is no difficulty in the movement of
the brush, then it is assessed as “Without obstacle in the second pass of brush coating”.
5.5.4 Low-temperature stability
Carry out 3 cycles of test in accordance with Method A of GB/T 9268-2008.
5.5.5 Low-temperature film-for...