QC/T 946-2024: Safety belt strap
QC/T 946-2024
QC
AUTOMOTIVE INDUSTRY STANDARD
OF THE PEOPLE’S REPUBLIC OF CHINA
ICS 43.040.60
CCS T 26
Replacing QC/T 946-2013
Safety Belt Strap
ISSUED ON: JULY 19, 2024
IMPLEMENTED ON: JANUARY 1, 2025
Issued by: Ministry of Industry and Information Technology of the People’s
Republic of China.
Table of Contents
Foreword ... 3
1 Scope ... 5
2 Normative References ... 5
3 Terms and Definitions ... 6
4 Technical Requirements ... 6
5 Test Methods ... 9
6 Inspection Rules ... 15
7 Marking, Packaging, Transportation and Storage ... 17
Safety Belt Strap
1 Scope
This document specifies the technical requirements, test methods, inspection rules, as well as
marking, packaging, transportation and storage, etc. of safety belt strap.
This document is applicable to the design, development, production, test and acceptance
inspection of strap used for automobile safety belt.
2 Normative References
The content of the following documents constitutes indispensable clauses of this document
through normative references in the text. In terms of references with a specified date, only
versions with a specified date are applicable to this document. In terms of references without a
specified date, the latest version (including all the modifications) is applicable to this document.
GB/T 250 Textiles - Tests for Color Fastness - Grey Scale for Assessing Change in Color
GB/T 251 Textiles - Tests for Color Fastness - Grey Scale for Assessing Straining
GB/T 1220 Stainless Steel Bars
GB/T 2828.1 Sampling Procedures for Inspection by Attributes - Part 1: Sampling Schemes
Indexed by Acceptance Quality Limit (AQL)
GB/T 3920 Textiles - Tests for Color Fastness - Color Fastness to Rubbing
GB/T 3922 Textiles - Tests for Color Fastness - Color Fastness to Perspiration
GB 8410 Flammability of Automotive Interior Materials
GB/T 8427-2019 Textiles - Tests for Color Fastness - Color Fastness to Artificial Light: Xenon
Arc
GB/T 30512 Requirements for Prohibited Substances on Automobiles
GB 38262 Flammability of Interior Materials for Buses
GB/T 39897-2021 Determination of Volatile Organic Compounds and Aldehydes and Ketones
in Nonmetallic Parts of Vehicles
QC/T 236 Test Method for Automotive Interior Decorative Material Properties
FZ/T 60045-2014 Textile Trim Materials in the Interior of Automobiles - Test Method for
Fogging Characteristics
3 Terms and Definitions
The following terms and definitions are applicable to this document.
3.1 strap
A flexible component used to restrain the occupant’s body and transmit the force received to
the seat belt anchorage point.
3.2 diagonal belt
A strap that goes diagonally across the chest from the hips to the other shoulder.
3.3 lap belt
A strap that goes across the front of the wearer’s pelvic area.
3.4 continuous belt
A strap with the diagonal belt and the lap belt made of one piece.
4 Technical Requirements
4.1 General Requirements
4.1.1 The safety belt strap shall comply with the requirements of this document, and the product
drawings shall be approved for manufacturing in accordance with the prescribed procedures.
4.1.2 The specifications of the strap thickness shall be determined by the supply-side and the
demand-side through negotiation.
4.1.3 When the strap is tested in accordance with the provisions of 5.2, the width of the strap
shall not be less than 46 mm.
4.2 Requirements for Properties
4.2.1 Tensile load
When the strap is tested in accordance with the provisions of 5.1.2, the tensile load of two
specimens shall not be less than the provisions of Table 1. The difference in the tensile load
between the two specimens shall not exceed 10% of the greater value of the measured tensile
load.
4.2.7 Wear resistance
After the strap is tested in accordance with the provisions of 5.9, its tensile load shall not be
less than 75% of the average tensile load measured in 5.1 and shall not be lower than 17,700 N
(for the diagonal belt, it shall not be lower than 14,700 N). The difference in the tensile load
between the two specimens shall not exceed 20% of the greater value of the measured tensile
load.
4.2.8 Color fastness
4.2.8.1 Color fastness to dry rubbing
The color fastness of the strap to dry rubbing shall not be lower than Level 4 specified in GB/T
251.
4.2.8.2 Color fastness to wet rubbing
The color fastness of the strap to wet rubbing shall not be lower than Level 4 specified in GB/T
251.
4.2.8.3 Color fastness to perspiration
The color fastness of the strap to dry rubbing shall not be lower than Level 4 specified in GB/T
251.
4.2.8.4 Color fastness to light
The color fastness of the strap to light shall not be lower than Level 4 specified in GB/T 250.
4.2.9 Flammability
The flammability of the strap for Category-M2 and Category-M3 passenger cars shall comply
with the relevant provisions of GB 38262, and the flammability of the strap for other types of
vehicles shall comply with the relevant provisions of GB 8410.
4.2.10 Prohibited substances
The prohibited substances shall comply with the relevant provisions of GB/T 30512.
4.2.11 Dispersion of volatile organic components and aldehyde and ketone components
The dispersion of volatile organic components and aldehyde and ketone components from the
strap shall not be greater than the limits in Table 3.
light for a time corresponding to the time required to fade blue wool standard 7 to
grey scale 4.
c) After light treatment, the strap shall be stored in an environment with a temperature
of 20 C  5 C and a relative humidity of 65%  5% for at least 24 hours, and shall
be measured within 5 minutes of being removed from the treatment environment.
d) Each strap shall be clamped between the fixtures of the tensile machine, with a
loading speed of 100 mm/min. Apply the load, until the strap breaks, and record the
breaking load value.
5.6 Low-temperature Resistance
5.6.1 Test conditions
The strap shall be stored in an environment with a temperature of 20 C  5 C and a relative
humidity of 65%  5% for at least 24 hours.
5.6.2 Test steps
The test shall be carried out in accordance with the following steps:
a) For each test, the strap treated in accordance with the provisions of 5.6.1 shall be used;
b) The strap shall be stored on a flat surface in a low-temperature chamber with a
temperature of 30 C  5 C for at least 1.5 hours;
c) Fold the strap in half, press a 2 kg weight block that has been pre-cooled to 30 C 
5 C on the folded part, and place it in the same low-temperature chamber for 30
minutes. After removing the weight block, the tensile load shall be measured within
5 minutes after the strap is removed from the low-temperature chamber;
d) The folded part of each strap shall be clamped between the fixtures of the tensile
testing machine. The loading speed is 100 mm/min. Apply the load, until the strap
breaks, and record the breaking load value.
5.7 High-temperature Resistance
5.7.1 Test conditions
The strap shall be stored in an environment with a temperature of 20 C  5 C and a relative
humidity of 65%  5% for at least 24 hours.
5.7.2 Test steps
The test shall be carried out in accordance with the following steps:
a) For each test, the strap treated in accordance with the provisions of 5.7.1 shall be used;
b) The strap shall be stored at a high temperature of 80 C  5 C and a relative humidity
of 65%  5% for 3 hours;
c) The t...